Fastener special quality inspection and control

Source:ZheKun Time2012-7-11 15:16:40 Author:admin View:5629

The special fasteners quality inspection of fasteners, heat treatment, in addition to the general quality inspection and control, there are some special quality inspection and control.
One, decarburization and Carburization
In the mass production of heat treatment process, metallographic micro-hardness method or, or, is the only regular sampling.Because the examination time is long, high cost.In order to determine the carbon control, can spark detection and Rockwell hardness testing on Decarburization and carburization made preliminary judgement.Spark testing is to quench fire parts, in sanding machine grinding sparks from the outside to the inside surface gently discrimination and heart of the carbon content is consistent.Of course, this requires the operator to have skilled and spark ability.Rockwell hardness testing in six angle bolt on one side of.The quenching over parts of a six angle plane polished with sandpaper lightly, first time hardness measurement.Then the surface grinder remove about 0.5mm, retest time hardness.If the two hardness is basically the same, that neither, nor carburization decarburization.After the previous is lower than the hardness hardness, description of surface decarbonization.The last time that is higher than the hardness, surface carburization.In general, the two hardness difference within 5HRC, by metallography and micro-hardness method inspection, parts of the decarbonization or carburizing basic qualified in the area.
In two, the hardness and strength
The threaded fastener detection, cannot simple according to hardness, relevant manuals, converted into intensity value.This is the middle of a hardenability factor.Because the national standards and national standards GB3098.1 specified in the GB3098.3 arbitration hardness is in part cross section 1/2 radius measurement.Tensile test specimen is from 1/2 radius interception.Because do not rule out the parts of the center section has low hardness, low intensity part of existence.
In general, material good hardenability, screw part cross section hardness can be evenly distributed.As long as the hardness of qualified, strength and that stress can also meet the requirement.But when the material hardenability is poor, although according to the provisions of the site inspection, hardness is qualified, but the intensity and ensure the stress often fail to meet the requirements.Especially the surface hardness tends to lower limit.
In order to ensure the strength and stress control in an acceptable range, often to increase the hardness of the lower limit value.As of 8.8 the hardness control range: the M16 following the specifications for the 26~31HRC, M16 above the specifications for the 28~34HRC is appropriate; 10.9 level control should be 36~39HRC.More than 10.9 are a different matter.
In three, then tempering
8.8~12.9 bolts, screws and studs, should be based on the actual production of the lowest tempering low temperature tempering at 10 ℃ for 30min again test.In the same sample, test and three point average hardness value difference of not more than 20HV.
Then tempering can check for quenching hardness inadequacy, with low temperature tempering hardness range to barely reached the incorrect operation, guarantee the components the comprehensive mechanical properties.Especially low carbon martensite steel threaded fasteners, adopting low temperature tempering, although other mechanical properties can be