45 steel and 40Cr steel quenching and tempering heat treatment process

Source:ZheKun Time2012-7-11 15:07:21 Author:admin View:8331

In 45 steel and 40Cr steel quenched and tempered heat treatment quenching and high temperature tempering, tempering is a dual heat treatment, its purpose is to make the workpiece has good comprehensive mechanical properties.
Quenched and tempered steel carbon steel and alloy steel two categories, either carbon steel or alloy steel, the carbon content control strictly.If the carbon content is too high, after tempering and the strength of the workpiece is high, but its toughness is not enough, such as the carbon content is too low, the toughness and intensity insufficient.In order to make the modified parts get good comprehensive performance, general carbon content control in 0.30~0.50%.
Quenching, the whole cross section of workpiece quenching, the quenching to obtain the fine acicular martensite.Through the high temperature tempering, get to evenly tempered sorbite in the microstructure.Small factories could not engage each furnace metallographic analysis, hardness test only, that is to say, the quenched hardness must reach the material hardness.
Workpiece quenching and tempering treatment operation, must strictly according to the process documents, we are just on the process how to implement process some views.
1, 45 steel, Quenched and tempered
45 steel is medium carbon structural steel, hot and cold processing performance are good, good mechanical properties, low price, wide source, so the application of broad.Its greatest weakness is the hardenability is low, large cross section size and relatively high requirements for the workpiece can not be used.
45 steel and 40Cr steel quenching and tempering heat treatment process of 45 steel, quenching temperature in A3 + (30~50) ℃, in actual operation, usually take the cap.High quenching temperature can make the workpiece heating speed, surface oxidation reduction, and can improve the work efficiency.For the austenite homogenization, need enough holding time.If the actual loading capacity is large, it necessary to prolong the time of heat preservation.Otherwise, may occur due to uneven heating caused by inadequate hardness phenomenon.But the holding time is too long, will also appear coarse grain, oxidation and decarbonization serious malady, the effects of quenching quality.We think, such as loading capacity is greater than the process documents, heating time extended 1/5.
Because the 45 steel hardenability is low, so it should be used in cooling rate in 10% saline solution.The workpiece into the water, should be quenched, but not cold, if the workpiece in salt water in the cold, it is possible to make the workpiece to crack, this is because when the workpiece is cooled to 180 ℃, austenite transforms into martensite quickly cause excessive tissue stress induced by.Therefore, when rapid cooling to the temperature quenching area, should take slow cooling method.The outlet temperature of difficult to grasp, to operation by experience, when the workpiece the wobble ceases, then water air cooling (such as oil cold better).In addition, the workpiece into the water to move is not static, should be in accordance with the workpiece geometry, as the rules of the sport.Stationary cooling medium coupled to the stationary workpiece, resulting in uneven hardness uneven stress, the deformation of the workpiece, and even cracking.
45 steel quenching hardness after quenching and tempering should reach HRC56~59, a large section low likelihood of some, but not less than HRC48, otherwise, that the workpiece is not fully hardened, tissues may appear even ferrite sorbite organization, this organization